Shofu Hy-Bond Resiglass
5 in stock
- Resin Modified Glass Ionomer Luting Cement (Luting)
$36.25 $42.00
5 in stock
A newly formulated radiopaque, Resin Modified Glass Ionomer (RMGI) Cement for luting metal-ceramic, full metal and metal-free crowns, bridges, inlays and onlays as well as orthodontic bracket
INDICATION:
- Cementation of metal based inlays,crowns & bridges
- Cementation of resin based inlays,crowns & bridges
- Cementation of ceramic (pocelain) based inlays,crowns & bridges
- Cementation of orthodontic (metal or ceramic) brackets and band
COMPOSITION:
POWDER:
- Fluoroaluminosilicate glass
- Additives
- Pigments
LIQUID:
- Polyacrylic acid
- Purified water
- 2- HEMA
- Mixing time 20sec
- working time 3min 30 sec
- setting time 7 min
STORAGE
store at room temperature: 1-30 degree celcius/34-86 F.
Features
- Chemically bonds to tooth structure to ensure higher bonding strength
- Fluoride Release & Biocompatible.
- Low film thickness of just 12μ
- Minimum odour and virtually no post-operative sensitivity
- Improved fracture toughness and low solubility for intra-oral durability of the restoration
- Provides an excellent marginal seal and prevents microleakage
- Exhibits high translucency for aesthetic cases
- Long working time with a net setting time of 4 minutes
- Change of colour from a light pink to colourless upon setting, for ease of identification and application.
- Easy to manipulate and remove excess cement.
Packaging
- 1 x 15gm Powder
- 1 x 8.6ml Liquid
- Mixing Pad.
Directions To Use
STEP1- Remove temporary material
Thoroughly remove the temporary filling materials. Rinse with water and dry.
STEP2- Pulp capping
In cases where the cavity is deep, application of calcium hydroxide
STEP3- Prepare the restoration. Clean the area to be cemented.
STEP4- Dispense the powder/liquid in standard ratio- 1.6g/1g
STEP5- Mix the prescribed powder liquid ratio on the mixing pad using plastic spatula for 20seconds.
working time 3min 30 sec
setting time 7 min
STEP6- Remove excess cement using an instrument.
when the excess material exhibit rubbery elasticity ( 2min 30sec- 3min 30 sec) remove it with the instrument.